Physical PropertiesMetricEnglishCommentsMechanical PropertiesMetricEnglishCommentsElectrical PropertiesMetricEnglishCommentsThermal PropertiesMetricEnglishComments
Specific Gravity | 1.08g/cc | 1.08g/cc | ASTM D 792 |
Water Absorption | 0.0700 % | 0.0700 % | 24 hrs; ASTM D 570 |
|
Hardness, Rockwell R | 113 | 113 | ASTM D 785 |
Tensile Strength, Yield | 42.0MPa | 6090psi | Type I, 50 mm/min; ASTM D 638 |
Elongation at Break | 50.0 % | 50.0 % | Type I, 50 mm/min; ASTM D 638 |
Flexural Modulus | 2.27GPa | 329ksi | 2.6 mm/min, 100 mm span; ASTM D 790 |
Flexural Yield Strength | 67.0MPa | 9720psi | 2.6 mm/min, 100 mm span; ASTM D 790 |
Gardner Impact | 13.0J @Temperature -40.0 °C | 9.59ft-lb @Temperature -40.0 °F | ASTM D 3029 |
| 24.0J @Temperature -30.0 °C | 17.7ft-lb @Temperature -22.0 °F | ASTM D 3029 |
Izod Impact, Notched | 1.60J/cm @Temperature -40.0 °C | 3.00ft-lb/in @Temperature -40.0 °F | ASTM D 256 |
| 3.89J/cm @Temperature 23.0 °C | 7.29ft-lb/in @Temperature 73.4 °F | ASTM D 256 |
|
Dielectric Constant | 2.80 | 2.80 | ASTM D 150 |
Dielectric Strength | 24.8kV/mm @Thickness 3.20 mm | 630kV/in @Thickness 0.126 in | in oil; ASTM D 149 |
Dissipation Factor | 0.00400 | 0.00400 | ASTM D 150 |
| 0.00350 @Frequency 1.00e+6 Hz | 0.00350 @Frequency 1.00e+6 Hz | IEC 60250 |
Arc Resistance | <=60.0sec | <=60.0sec | Tungsten; PLC Code 7; ASTM D 495 |
Comparative Tracking Index | 250-400V | 250-400V | UL 746A |
Hot Wire Ignition, HWI | 60.0-120sec | 60.0-120sec | PLC 1; UL 746A |
High Amp Arc Ignition, HAI | >=120arcs | >=120arcs | surface; UL 746A |
High Voltage Arc-Tracking Rate, HVTR | >=150mm/min | >=5.91in/min | PLC 4; UL 746A |
|
CTE, linear | 73.8µm/m-°C @Temperature -40.0 - 95.0 °C | 41.0µin/in-°F @Temperature -40.0 - 203 °F | Flow; ASTM E 831 |
Deflection Temperature at 0.46 MPa (66 psi) | 93.0°C @Thickness 6.40 mm | 199°F @Thickness 0.252 in | unannealed; ASTM D 648 |
Deflection Temperature at 1.8 MPa (264 psi) | 82.0°C @Thickness 6.40 mm | 180°F @Thickness 0.252 in | unannealed; ASTM D 648 |
UL RTI, Electrical | 50.0°C | 122°F | UL 746B |
UL RTI, Mechanical with Impact | 50.0°C | 122°F | UL 746B |
UL RTI, Mechanical without Impact | 50.0°C | 122°F | UL 746B |
Flammability, UL94 | V-1 @Thickness 1.49 mm | V-1 @Thickness 0.0587 in | UL 94 |
| V-0 @Thickness 2.99 mm | V-0 @Thickness 0.118 in | UL 94 |
|